@article{oai:mie-u.repo.nii.ac.jp:00008427,
 author = {畑中, 重光 and HATANAKA, Shigemitsu and 三島, 直生 and MISHIMA, Naoki and 和藤, 浩 and WATOH, Hiroshi and 村松, 昭夫 and MURAMATSU, Akio and 山口, 武志 and YAMAGUCHI, Takeshi and 筒井, 文康 and TSUTSUI, Fumiyasu},
 issue = {35},
 journal = {日本建築学会技術報告集},
 month = {Feb},
 note = {application/pdf, Very fine plastic shrinkage crack is often reported to occur on vacuum processed concrete slab, which is considered due to cement-richness of a surface layer. A shrinkage-reduction admixture is used in order to prevent such plastic shrinkage cracks. Although the cracks can be avoided by this method, white powders of CaCO3 sometimes appear on the surface. The effects of the admixture and curing condition were investigated on the amount of powders and the bond strength. It was found that appropriate addition of the admixture successfully reduces the plastic shrinkage cracks without producing powders on the surface.},
 pages = {31--35},
 title = {真空脱水コンクリート床スラブの表層に発生する微細ひび割れの低減に関する実験的検討},
 volume = {17},
 year = {2011}
}