液漏れしない比較電極および琺瑯電極の開発
http://hdl.handle.net/10076/00020926
http://hdl.handle.net/10076/00020926dd18c708-5817-4f50-836d-666d02bb209c
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
2022RP0069 (654.5 kB)
|
|
| Item type | 報告書 / Research Paper(1) | |||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2022-11-29 | |||||||||||||||||||||||
| タイトル | ||||||||||||||||||||||||
| タイトル | 液漏れしない比較電極および琺瑯電極の開発 | |||||||||||||||||||||||
| 言語 | ja | |||||||||||||||||||||||
| タイトル | ||||||||||||||||||||||||
| タイトル | Development of Referenc Electrodes without Internal Liquid Leakage and Enamel Electrodes | |||||||||||||||||||||||
| 言語 | en | |||||||||||||||||||||||
| 言語 | ||||||||||||||||||||||||
| 言語 | jpn | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | pH応答電極 | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | ガラス電極 | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | 金属電極 | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | 琺瑯電極 | |||||||||||||||||||||||
| キーワード | ||||||||||||||||||||||||
| 主題Scheme | Other | |||||||||||||||||||||||
| 主題 | 比較電極 | |||||||||||||||||||||||
| 資源タイプ | ||||||||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||||||||||||||||||||
| 資源タイプ | research report | |||||||||||||||||||||||
| 著者 |
橋本, 忠範
× 橋本, 忠範
× 石原, 篤
× 那須, 弘行
|
|||||||||||||||||||||||
| 抄録 | ||||||||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||||||||
| 内容記述 | 液漏れしない比較電極に関しては，xAg(100-x)Teガラスがこれまでのガラスと比較して，比較電極に適していることがわかった。さらに加熱した25Ag75Teガラスはより適していることがわかった。この原因は，正方晶のAgの析出と関係づけられた。 琺瑯電極に関しては，25Ag75Te/ステンレス構造とすることで本研究の中で最も比較電極に適した電極を得ることに成功した。この原因は，比較的珍しい六方晶のAg（もしくはAg2Te）の析出と関係づけられた。 |
|||||||||||||||||||||||
| 抄録 | ||||||||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||||||||
| 内容記述 | An Ag/AgCl reference electrode that is built into commercially available pH electrodes leaks its internal KCl solution via a liquid junction. This leakage is disadvantageous because the test solution is contaminated by a trace amount of the KCl solution. The applicability of Ag2O-TeO2 glasses to reference electrodes for pH sensors was investigated in this study. The effects of the Ag2O content and heat treatment on the pH sensitivity of these glasses and the pH sensitivity of the Ag2O-TeO2 glass/stainless steel electrodes were examined. The pH sensitivity of Ag2O-TeO2 glasses increased as the Ag2O content increased, but it was less than 40 % and was the lowest among the glasses that have been investigated to date. The 25Ag2O･75TeO2 glass/stainless steel electrodes precipitated cubic Ag and hexagonal Ag and showed relatively low pH sensitivities of 26 % and 5 %, respectively. Thus, the hexagonal Ag-precipitated samples were considered candidate reference electrodes for pH sensors. | |||||||||||||||||||||||
| 内容記述 | ||||||||||||||||||||||||
| 内容記述タイプ | Other | |||||||||||||||||||||||
| 内容記述 | 2018年度～2020年度科学研究費補助金(基盤研究(C))研究成果報告書 | |||||||||||||||||||||||
| 書誌情報 |
発行日 2021-05-13 |
|||||||||||||||||||||||
| フォーマット | ||||||||||||||||||||||||
| 内容記述タイプ | Other | |||||||||||||||||||||||
| 内容記述 | application/pdf | |||||||||||||||||||||||
| 著者版フラグ | ||||||||||||||||||||||||
| 出版タイプ | VoR | |||||||||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||||||||||||||||
| 出版者 | ||||||||||||||||||||||||
| 出版者 | 三重大学 | |||||||||||||||||||||||
| 出版者（ヨミ） | ||||||||||||||||||||||||
| ミエダイガク | ||||||||||||||||||||||||
| 科研費番号 | ||||||||||||||||||||||||
| 内容記述タイプ | Other | |||||||||||||||||||||||
| 内容記述 | 18K04702 | |||||||||||||||||||||||
| 資源タイプ（三重大） | ||||||||||||||||||||||||
| Kaken / 科研費報告書 | ||||||||||||||||||||||||