WEKO3
アイテム
超軽量カルシウム－リチウム系ラーベス相合金の水素化特性
http://hdl.handle.net/10076/13762
http://hdl.handle.net/10076/137628735fcb0-d271-400b-b88c-2430d0dbee75
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
20K16705.pdf (491.0 kB)
|
|
| Item type | 報告書 / Research Paper(1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2014-03-10 | |||||||||
| タイトル | ||||||||||
| タイトル | 超軽量カルシウム－リチウム系ラーベス相合金の水素化特性 | |||||||||
| 言語 | ja | |||||||||
| 言語 | ||||||||||
| 言語 | jpn | |||||||||
| キーワード | ||||||||||
| 主題Scheme | Other | |||||||||
| 主題 | 水素貯蔵合金 | |||||||||
| キーワード | ||||||||||
| 主題Scheme | Other | |||||||||
| 主題 | ラーベス相 | |||||||||
| キーワード | ||||||||||
| 主題Scheme | Other | |||||||||
| 主題 | CaLi2 | |||||||||
| キーワード | ||||||||||
| 主題Scheme | Other | |||||||||
| 主題 | 複合化 | |||||||||
| キーワード | ||||||||||
| 主題Scheme | Other | |||||||||
| 主題 | ペロブスカイト型水素化物 | |||||||||
| 資源タイプ | ||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||||||
| 資源タイプ | research report | |||||||||
| 著者 |
牧原, 義一
× 牧原, 義一
|
|||||||||
| 抄録 | ||||||||||
| 内容記述タイプ | Abstract | |||||||||
| 内容記述 | CaLi_2を母合金とする新たな置換系化合物群を系統的に合成し,その結晶構造と水素化特性および水素吸蔵放出に伴う結晶構造変化を明らかにした。今回作製したCaLi_2基の置換型化合物群では,可逆的に水素を吸蔵放出する化合物を発見することはできなかったが,室温で5～7mass%の多量の水素と反応する新たな単相C14相化合物群を見出すことができた。CaLi_2とLaNi_5を用いて,アーク溶解法,高周波溶解法およびボールミリング法により新規水素化物の合成を試みた。いずれの方法においても,CaLi_2とLaNi_5の新規複合化物質が得られ,特にボールミリング法による複合化物の水素化特性は興味深い性質を示すものと期待される。CaLi_2をベースにした水素雰囲気下でのメカニカルミリングによる新規ペロブスカイト型水素化物の探索を行い,結晶性の良いペロブスカイト型水素化物SrLiH_3およびBaLiH_3を得ることができた。 | |||||||||
| 抄録 | ||||||||||
| 内容記述タイプ | Abstract | |||||||||
| 内容記述 | New series of intermetallic compounds which are replaced a part of Laves phase CaLi_2 with other elements were synthesized systematically. The structural and hydrogen storage properties of them were investigated. We found new series of C14-type Laves phase compounds which absorb much hydrogen of 5～7 mass% at room temperature. Unfortunately, no samples prepared show the reversible property of hydrogen absorbing and desorbing. Using the arc melting, the induction melting and the mechanical milling methods, respectively, new composites of CaLi_2 and LaNi_5 were synthesized. It is expected that interesting hydriding properties are found out in the samples prepared by the mechanical milling method, because the XRD pattern of them show only peaks indexed by the reflection from LaNi_5. New perovskite-type hydrides were synthesized by milling the mixed powders of CaLi_2 and MgH_2, SrH_2 and BaH_2, respectively, in a hydrogen atmosphere of 3 MPa. Perovskite-type hydrides of SrLiH_3 and BaLiH_3 with high purity crystallization were prepared by this method. | |||||||||
| 内容記述 | ||||||||||
| 内容記述タイプ | Other | |||||||||
| 内容記述 | 平成20~22年度科学研究費補助金(基盤研究(C))研究成果報告書 | |||||||||
| 書誌情報 |
発行日 2011-04-21 |
|||||||||
| フォーマット | ||||||||||
| 内容記述タイプ | Other | |||||||||
| 内容記述 | application/pdf | |||||||||
| 著者版フラグ | ||||||||||
| 出版タイプ | VoR | |||||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||||
| その他のタイトル | ||||||||||
| Structural and Hydrogen Storage Properties of Extremely Lightweight Compounds Synthesized from Laves Phase CaLi_2 Based System | ||||||||||
| 出版者 | ||||||||||
| 出版者 | 三重大学 | |||||||||
| 科研費番号 | ||||||||||
| 内容記述タイプ | Other | |||||||||
| 内容記述 | 20560651 | |||||||||
| 資源タイプ（三重大） | ||||||||||
| Kaken / 科研費報告書 | ||||||||||